1.21 | g/cm3 | ASTM D792 | |
Specific Volume | 0.830 | cm3/g | ASTM D792 |
1.22 | g/cm3 | ISO 1183 | |
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 15.0 | cm3/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.80 to 1.0 | % | Internal Method |
Molding Shrinkage - Across Flow 2 | 0.80 to 1.0 | % | Internal Method |
Water Absorption (Saturation, 23°C) | 0.50 | % | ISO 62 |
Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | ISO 62 |
f2 | UL 746C | ||
| Mechanical | Nominal Value | Unit | Test Method |
| ASTM D638 | |||
-- 3 | 2250 | MPa | |
-- 4 | 2250 | MPa | |
2050 | MPa | ISO 527-2/1 | |
Tensile Strength 5 (Yield) | 53.0 | MPa | ASTM D638 |
Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/50 |
Tensile Strength 5 (Break) | 51.0 | MPa | ASTM D638 |
Tensile Stress (Break) | 50.0 | MPa | ISO 527-2/50 |
Tensile Elongation 5 (Yield) | 4.0 | % | ASTM D638 |
Tensile Strain (Yield) | 4.0 | % | ISO 527-2/50 |
Tensile Elongation 5 (Break) | 120 | % | ASTM D638 |
Tensile Strain (Break) | 120 | % | ISO 527-2/50 |
Flexural Modulus 6 (50.0 mm Span) | 2030 | MPa | ASTM D790 |
2000 | MPa | ISO 178 | |
Flexural Stress 7, 8 | 80.0 | MPa | ISO 178 |
Flexural Strength 6 (Yield, 50.0 mm Span) | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 9 (23°C) | 55 | kJ/m2 | ISO 179/1eA |
| ASTM D256 | |||
-40°C | 300 | J/m | |
-30°C | 530 | J/m | |
23°C | 710 | J/m | |
| ISO 180/1A | |||
-30°C | 30 | kJ/m2 | |
23°C | 50 | kJ/m2 | |
Instrumented Dart Impact (23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 107 | °C | ASTM D648 |
| ASTM D648 | |||
1.8 MPa, Unannealed, 3.20 mm | 84.0 | °C | |
1.8 MPa, Unannealed, 6.40 mm | 99.0 | °C | |
Heat Deflection Temperature 11 (1.8 MPa, Unannealed, 64.0 mm Span) | 75.0 | °C | ISO 75-2/Af |
122 | °C | ASTM D1525 12 | |
-- | 120 | °C | ISO 306/B50 |
-- | 125 | °C | ISO 306/B120 |
CLTE - Flow (-40 to 40°C) | 9.5E-5 | cm/cm/°C | ASTM E831 |
CLTE - Flow (-40 to 40°C) | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
CLTE - Transverse (-40 to 40°C) | 9.0E-5 | cm/cm/°C | ASTM E831 |
CLTE - Transverse (-40 to 40°C) | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
75.0 | °C | UL 746 | |
75.0 | °C | UL 746 | |
75.0 | °C | UL 746 | |
| Electrical | Nominal Value | Unit | Test Method |
PLC 5 | ASTM D495 | ||
PLC 1 | UL 746 | ||
PLC 0 | UL 746 | ||
PLC 0 | UL 746 | ||
PLC 3 | UL 746 | ||
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating (1.50 mm) | HB | UL 94 |
| Processing Information | |||
| Injection | Nominal Value | ||
Drying Temperature | 110 | ||
Drying Time | 4.0 to 6.0 | ||
Drying Time, Maximum | 8.0 | ||
Suggested Max Moisture | 0.020 | ||
Suggested Shot Size | 50 to 80 | ||
Rear Temperature | 243 to 266 | ||
Middle Temperature | 249 to 271 | ||
Front Temperature | 254 to 277 | ||
Nozzle Temperature | 254 to 271 | ||
Processing (Melt) Temp | 260 to 277 | ||
Mold Temperature | 65.6 to 87.8 | ||
Back Pressure | 0.345 to 0.689 | ||
Screw Speed | 50 to 80 | ||
Vent Depth | 0.013 to 0.020 | ||
| Extrusion | Nominal Value | ||
Drying Temperature | 110 to 116 | ||
Drying Time | 4.0 to 6.0 | ||
Suggested Max Moisture | 1.0E-3 to 0.020 | ||
Cylinder Zone 1 Temp. | 171 to 204 | ||
Cylinder Zone 2 Temp. | 193 to 254 | ||
Cylinder Zone 3 Temp. | 204 to 282 | ||
Cylinder Zone 4 Temp. | 204 to 282 | ||
Adapter Temperature | 227 to 282 | ||
Melt Temperature | 243 to 277 | ||
Die Temperature | 232 to 282 | ||
| Extrusion Notes | |||
Drying Time (Cumulative): 8 hrs Roll Stack Temp - Bottom: 82 - 93 °C Roll Stack Temp - Middle: 77 - 82 °C Roll Stack Temp - Top: 71 - 82 °C | |||