产品参数
| 性能项目 | 测试方法 | 试验条件[状态] | 测试数据 | 数据单位 | |
| 性能 | 拉伸强度 | ASTM D638 | 22.0 152 | kpsi Mpa | |
| 拉伸模量 | ASTM D638 | 650 4.5 | kpsi GPa | ||
| 拉伸伸长率 | ASTM D638 | 7.6 | % | ||
| 挠曲强度 | ASTM D790 | 34.9 244 | kpsi Mpa | ||
| 挠曲模量 | ASTM D790 | 730 5.0 | kpsi GPa | ||
| 压缩强度 | ASTM D695 | 32.1 221 | kpsi Mpa | ||
| 剪切强度 | ASTM D732 | 18.5 128 | kpsi Mpa | ||
| 悬臂梁式冲击，有缺口 | ASTM D256 | 2.7 140 | ft-lb/in J/m | ||
| 悬臂梁式冲击，无缺口 | ASTM D4812 | 20 1060 | ft-lb/in J/m | ||
| 热变形温度 | 264psi,ASTM D 648 | 278 532 | ℃ ℉ | ||
| CLTE3 | ASTM D 696 | 31 17 | ppm/℃ ppm/℉ | ||
| 体积电阻率 | ASTM D 257 | 2X107 | ohm-cm | ||
| 比重 | ASTM D 792 | 1.42 | |||
| 吸水性，24小时 | ASTM D 570 | 0.33 | % | ||
| 摩擦系数，干摩擦50fpm（0.25m/s) | ASTM D 3702 | 0.31 | |||
| 摩擦系数，干摩擦800fpm(4m/s) | ASTM D 3702 | 0.29 | |||
| 摩损系数，干摩擦350fpm（0.25m/s) | ASTM D 3702 | 13 23 | 10-10in3min/ft-lb-hr 10-8mm3/Nm | ||
| 摩损系数，干摩擦3800fpm(4m/s) | ASTM D 3702 | 18 32 | 10-10in3min/ft-lb-hr 10-8mm3/Nm | ||
| 摩损系数，润滑环境4 | ASTM D 3702 | 7 12 | 10-10in3min/ft-lb-hr 10-8mm3/Nm | ||